Objective To investigate the cellular compatibil ity of polyvinyl alcohol (PVA)/wild antheraea pernyisilk fibroin (WSF), and to explore the feasibil ity for tendon tissue engineering scaffold in vitro. Methods The solutions of WSF (11%), PVA (11%), and PVA/WSF (11%) were prepared with 98% formic acid (mass fraction) at a mass ratio of 9 : 1. The electrospinning membranes of WSF, PVA, and PVA/WSF were prepared by electrostatic spinning apparatus. The morphologies of scaffolds were evaluated using scanning electronic microscope (SEM). The tendon cells were isolated from tail tendon of 3-dayold Sprague Dawley rats in vitro. The experiment was performed using the 3rd generation cells. The tendon cells (1 × 106/mL) were cocultured with PVA and PVA/WSF electrospinning film, respectively, and MTT test was used to assess the cell adhesion rate 4, 12 hours after coculture. The tendon cells were cultured in PVA and PVA/WSF extraction medium of different concentration (1, 1/2, and 1/4), respectively; and the absorbance (A) values were detected at 1, 3, 5, and 7 days to evaluate the cytotoxicity. The composite of tendon cells and the PVA or PVA/WSF scaffold were observed by HE staining at 7 days and characterized by SEM at 1,3, 5, and 7 days. Results The solution of WSF could not be used to electrospin; and the solution of PVA and PVA/WSF could be electrospun. After coculture of tendon and PVA or PVA/WSF electrospinning membranes, the cell adhesion rates were 26.9% ±0.4% and 87.0% ± 1.0%, respectively for 4 hours, showing significant difference (t=100.400, P=0.000); the cell adhesion rates were 35.2% ± 0.6% and 110.0% ± 1.7%, respectively for 12 hours, showing significant difference (t=42.500, P=0.000). The cytotoxicity of PVA/WSF was less significantly than that of PVA (P lt; 0.05) and significant difference was observed between 1/2 PVA and 1/4
PVA (P lt; 0.05). HE staining and SEM images showed that the tendon cells could adhere to PVA and PVA/WSF scaffolds, but that the cells grew better in PVA/WSF scaffold than in PVA scaffold in vitro. Conclusion PVA/WSF electrospinning membrane scaffold has good cell compatibility, and it is expected to be an ideal scaffold of tendon tissue engineering.
Citation： WU Linlin,LI Min,ZHAO Jin,CHEN Denglong,ZHOU Zhihua. PRELIMINARY STUDY ON POLYVINYL ALCOHOL / WILD ANTHERAEA PERNYI SILK FIBROIN AS NANOFIBER SCAFFOLDS FOR TISSUE ENGINEERED TENDON. Chinese Journal of Reparative and Reconstructive Surgery, 2011, 25(2): 181-186. doi: Copy