Objective To investigate the osteogenesis effects of angiopoietin 1 (Ang-1) gene transfected bone marrow mesenchymal stem cells (BMSCs) seeded on β tricalcium phosphate (β-TCP) scaffolds (tissue engineered bone) with platelet-rich plasma (PRP). Methods BMSCs were isolated from bone marrow tissue of rabbits. The Ang-1 gene was transfected into the BMSCs at passage 2 by lentivector, which were seeded on β-TCP scaffolds with PRP (0.5 mL) after 48 hours of transfection. Bilateral radial segmental bone defects (15 mm in length) were created in 20 3-month-old New Zealand rabbits. Then the tissue engineered bone with the Ang-1 gene transfected BMSCs (experimental group) and untransfected BMSCs (control group) were implanted into the defects in the right and left radius, respectively. X-ray, histology, immunohistochemistry, and biomechanics observations were done at 2, 4, 8, and 12 weeks after operation. Results In vitro, the transfected rate was over 90% and RT-PCR showed that the Ang-1 expression were significantly increased after transfection. The X-ray films showed that some callus formed at 4 weeks, partial bony union was observed at 8 weeks, and complete union at 12 weeks in experimental group; and bone union was not observed at 12 weeks in control group. HE staining showed that capillary appeared at 8 weeks and more capillaries were observed in new bone at 12 weeks in experimental group; only a few capillaries were observed at 12 weeks in control group. At 8 and 12 weeks, the microvascular density were (50.1 ± 7.8) /mm2 and (66.1 ± 3.5) /mm2 in experimental group and were 0 and (30.3 ± 7.2)/mm2 in control group, showing significant differences between 2 groups at 12 weeks (Z= —2.107, P=0.031). Immunohistochemistry examination showed that the positive cells can be found at 8 weeks in experimental group. And the biomechanical analysis showed that maximum loads of experimental group were significantly higher than those of control group in three-point bending test and compression test at 12 weeks (P lt; 0.05). Conclusion The tissue engineered bone with PRP and Ang-1 can increase the osteogenic properties by enhancing capillary regeneration, thus it can be used to repair radial segmental bone defects of rabbit.
Citation： LIU Xudong,CAO Le,JIANG Yao,ZENG Bingfang,ZHANG Changqing.. REPAIR OF RADIAL SEGMENTAL BONE DEFECTS BY COMBINED ANGIOPOIETIN 1 GENE TRANSFECTED BONE MARROW MESENCHYMAL STEM CELLS AND PLATELET-RICH PLASMA TISSUE ENGINEERED BONE IN RABBITS. Chinese Journal of Reparative and Reconstructive Surgery, 2011, 25(9): 1115-1119. doi: Copy