LI Baoqiang 1 , HUANG Yanming 2 , ZHANG Yuxi 1 , SUN Zhan 1
  • 1Institute for Advanced Ceramics, Harbin Institute of Technology, Harbin Heilongjiang, 150001, P.R.China;;
  • 2First Department of Orthopaedics, Heilongjiang Anti-tuberculosis Hospital;
Chitosan; Carboxymethyl chitosan; Glycerol; Etamsylate; Hemostatic material
Export PDF Favorites Scan Get Citation

Abstract Full text Figures/Tables References Cited by

Objective To improve the flexibil ity and hemostatic properties of chitosan (CS)/carboxymethyl chitosan (CMCS) hemostatic membrane by using glycerol and etamsylate to modify CS/CMCS hemostatic membrane. To investigate the
mechanical properties and hemostatic capabil ity of modified CS/CMCS hemostatic membrane. Methods The 2% CS solution, 2% CMCS solution, 10%, 15%, 20%, 25%, 30% glycerol with or without 0.5% etamsylate were used to prepare CS/CMCS hemostatic membrane with or without etamsylate by solution casting according to ratio of 16 ∶ 4 ∶ 5. The tensile properties were evaluated by tensile test according to GB 13022-1991. Twenty venous incisions and five arterial incisions hemorrhage of 1 cm × 1 cm in rabbit ears were treated by CS/CMCS hemostatic membrane modified by 15% (group A) and 25% (group B) of glycerol, and a combination of them and 0.5% etamsylate (groups C and D). The bleeding time and blood loss were recorded. Results The pH of yellow CS/ CMCS hemostatic membrane with thickness of 30-50 μm was 3-4. The incorporation glycerol into CS/CMCS hemostatic membrane resulted in decreasing in tensile strength (7.6%-60.2%) and modulus (97%-99%). However, elongation at break and water content increased 5.7-11.6 times and 13%-125% markedly. CS/CMCS hemostatic membrane adhered to wound rapidly, absorbed water from blood and became curly. The bleeding time and blood loss of venous incisions were (70 ± 3) seconds and (117.2 ± 10.8) mg, (120 ± 10) seconds and (121.2 ± 8.3) mg, (52 ± 4) seconds and (98.8 ± 5.5) mg, and (63 ± 3) seconds and (90.3 ± 7.1) mg in groups A, B, C, and D, respectively; showing significant differences (P  lt; 0.05) between groups A, B and groups C, D. The bleeding time and blood loss of arterial incision were (123 ± 10) seconds and (453.3 ± 30.0) mg in group C. Conclusion CS/CMCS hemostatic membrane modified by glycerol and etamsylate can improve the flexibil ity, and shorten the bleeding time.

Citation： LI Baoqiang,HUANG Yanming,ZHANG Yuxi,SUN Zhan. PREPARATION AND HEMOSTATIC EVALUATION OF CHITOSAN COMPOSITE HEMOSTATIC MEMBRANE.. Chinese Journal of Reparative and Reconstructive Surgery, 2010, 24(3): 340-343. doi: Copy