Objective To investigate the effect of tissue engineering bone compounded in vitro by nanohydroxyapatite/collagen/ polylactic acid (nHAC/PLA) and recombinant human bone morphogenetic protein 2 (rhBMP-2) in repairing rabbit critical calvarial defects. Methods Forty eight New Zealand rabbits, weighting 2.0-2.5 kg, were made the models of critical cranial defects(15 mm in diameter) and divided into 4 groups randomly. Defects were repaired with autoflank bone in the positive control group; with no implant in the blank control group; with nHAC/PLA in the negative control; and with active nHAC/PLA(AnHAC/PLA) in the experimental group(the average quality of each AnHAC/PLA absorbed rhBMP-2 was 1.431 mg). The reapir results were observed through X-ray,HE dyeing and Masson’s trichrism dyeing after 8 and 16 weeks. Results The difference of bone formation was observed by X-ray block degree of skull defect area at 8 and 16 weeks. In the 8 th week and 16 th week, the radiopacities on cranial defect were 67.21%±2.06% and 86.48%±1.73% in the positive control group; 5.84%±1.92% and 9.48%±2.72% in the blank control group; 19.13%±2.51% and 35.67%±3.28% in the negative control group; and 58.84%±2.55% and 8561%±3.36% in the experimental group. There were significant differences between the negative control and the positive control group, and between the experimental group and the positive control group at 8 weeks(P lt;0.05) . There were significant differences between the negative control and blank group, and between the experiment and the blank group at 8 and 16 weeks(P<0.05). The histology observation showed that the width of bone trabecula at 16 weeks was more than that at 8 weeks and bone defectwas full of bone tissue in positive control group. The bone defect was full of fibrous tissue at 8 and 16 weeks, and there was no new bone in the blank group. The bone defect was full of remnant material and fibrous tissue in the negative control group. The implanted area was replaced by the new bone at 8 weeks and the new bone was lamellar at 16 weeks in the experimental group; the residual material was less in defect area and there were more osteoblasts surrounding. Conclusion The nHAC/PLA is a good scaffoldmaterial of rhBMP-2 and AnHAC/PLA has agood ability in repairing bone defect. So it is hopeful to be applied in the clnical repair of large bone defect.

Citation: CHEN Peng,LIU Bing.. STUDY ON REPAIR OF CRITICAL CALVARIAL DEFECTS WITH NANOHYDROXYAPATITE/COLLAGEN/POLYLACTIC ACID MATERIAL COMPOUNDED RECOMBINANT HUMANBONE MORPHOGENETIC PROTEIN 2 IN RABBITS. Chinese Journal of Reparative and Reconstructive Surgery, 2007, 21(11): 1191-1195. doi: Copy