Objective To develop a novel porous three-dimensional scaffold and to investigate its physico-chemical properties for tissue engineering cartilage.Methods Refined 88% deacetylation degree chitosan was prepared and dissolved in 0.2 mol/L acetate acid and fully mixed with highly purified porcine type Ⅱcollagen in 0.5 mol/L acetate acid solution in a ratio of 4 to 1 (wt/wt). Freeze-drying process was employed to fabricate the composite scaffold. The construct wascross-linked by use of 1-ethyl-3(3-dimethyl aminopropyl) carbodiimide (EDC) and Nhydroxysuccinimide (NHS). A mechanical tester was utilized to determine the tensilestrength change before and after cross-linking. The microstructure was observed via scanning electron microscopy (SEM). The lysozyme degradation was performedto evaluate the degradability of the scaffold in vitro. Results A bulk scaffold with desired configuration was obtained. The mechanical test showed that the crosslinking treatment could enhance the mechanical strength of the scaffold. The SEM results revealed that the two constituents evenly distributed in the scaffold and that the matrix was porous, sponge-like with interconnected pore sizing 100250 μm. In vitro lysozyme degradation indicated that crosslinked or uncross-linked composite scaffolds had faster degradation rate than the chitosan matrix. Conclusion Chitosan and typeⅡcollagen can be developed into a porous three-dimensional scaffold. The related physico-chemical tests suggest that the composite socaffold meets requirements for tissue engineered scaffold and may serve as an alternative cellcarrier for tissue engineering cartilage.

Citation： SHI Dehai,CAI Daozhang,ZHOU Changren,et al.. FABRICATION AND PROPERTIES OF A COMPOSITE CHITOSAN/TYPE Ⅱ COLLAGEN SCAFFOLD FORTISSUE ENGINEERING CARTILAGE. Chinese Journal of Reparative and Reconstructive Surgery, 2005, 19(4): 278-282. doi: Copy