Objective To provide the chosen scaffold materials for experiment and application of tissue engineering and to detect the properties of the collagenbio-derived bone scaffold material loading WO-1. Methods The purebio-derived bone scaffold material, bio-derived bone scaffold material loading collagen, collagen bio-derived bone scaffold material loading WO-1 were made by use of allograftbone, and typeI collagen, and WO-1. The morphological features, constitute components and mechanical properties were examined by scanning electron microscopy,X- rays diffraction and mechanical assay. Results The bio-derived bone scaffold material maintained natural network pore system; the bio-derived bone scaffold material loading collagen maintained natural network pore system, the surface of network pore system was coated by collagen membrane; the collagen bio-derived bone scaffold material loading WO-1 maintained natural network pore system, thesurface of network pore system was coated by collagen membrane. The pore sizes of the 3materials were 90-700 μm, 75-600 μm and 80-600 μm, respectively, and the porosities were 87.96%, 80.47%, 84.2%. There was no significant difference between them(P＞0.05).The collagen bio-derived bone scaffold material loading WO-1 consisted of ［HA,Ca10(OH)2(PO4)6］. There was no significant difference in the mechanical strength of the three scaffold materials. Conclusion The bio-derived bone scaffold material loading WO-1 is as good as bio-derived bone scaffold material and collagen bio-derived bone scaffold material, and it is an effective scaffold material for tissue engineering bone.
Citation： LIANG Jun,YANG Zhiming,LI Xiuqun,etal.. EXPERIMENTAL STUDIES ON PREPARATION AND PROPERTY OF SCAFFOLD MATERIAL OF BIO-DERIVED BONE LOADING WO-1. Chinese Journal of Reparative and Reconstructive Surgery, 2005, 19(6): 464-467. doi: Copy