Objective To investigate the effect of allogeneic chondrocytes-calcium alginate gel composite under the intervention of low intensive pulsed ultrasound (LIPUS) for repairing rabbit articular cartilage defects. Methods Bilateral knee articular cartilage were harvested from 8 2-week-old New Zealand white rabbits to separate the chondrocytes by mechanical-collagen type II enzyme digestion. The 3rd passage chondrocytes were diluted by 1.2% sodium alginate to 5 × 106 cells/mL, then mixed with CaCl2 solution to prepare chondrocytes-calcium alginate gel composite, which was treated with LIPUS for 3 days (F0: 1 MHz; PRF: 1 kHz; Amp: 60 mW/cm2; Cycle: 50; Time: 20 minutes). An articular cartilage defect of 3 mm in diameter and 3 mm in thickness was established in both knees of 18 New Zealand white rabbits (aged 28-35 weeks; weighing, 2.1-2.8 kg), and divided into 3 groups randomly, 6 rabbits in each group: LIPUS group, common group, and model group. Defect was repaired with LIPUS-intervention gel composite, non LIPUS-intervention gel composite in LIPUS group and common group, respectively; defect was not treated in the model group. The general condition of rabbits was observed after operation. The repair effect was evaluated by gross and histological observations, immunohistochemical staining, and Wakitani score at 8 and 12 weeks after operation. Results Defect was filled with hyaline chondroid tissue and white chondroid tissue in LIPUS and common groups, respectively. LIPUS group was better than common group in the surface smooth degree and the degree of integration with surrounding tissue. Defect was repaired slowly, and the new tissue had poor elasticity in model group. Histological observation and Wakitani score showed that LIPUS group had better repair than common group at 8 and 12 weeks after operation; the repair effect of the 2 groups was significantly better than that of model group (P lt; 0.05); and significant differences in repair effect were found between at 8 and 12 weeks in LIPUS and common groups (P lt; 0.05). The collagen type II positive expression area and absorbance (A) value of LIPUS and common groups were significantly higher than those of model group (P lt; 0.05) at 8 and 12 weeks after operation, and the expression of LIPUS group was superior to that of common group at 12 weeks (P lt; 0.05); and significant differences were found between at 8 and 12 weeks in LIPUS group (P lt; 0.05), but no significant difference between 2 time points in common and model groups (P gt; 0.05). Conclusion Allogeneic chondrocytes-calcium alginate gel composite can effectively repair articular cartilage defect. The effect of LIPUS optimized allogeneic chondrocytes-calcium alginate gel composite is better.
Objective To investigate the effect of dynamic compression and rotation motion on chondrogenesis of the 3rd passage cell-loaded three-dimensional scaffold in a joint-specific bioreactor in vitro so as to provide theoretical basis of the autologous chondrocyte transplantation in clinical practice. Methods Primary chondrocytes were isolated and cultured from the knee cartilage of 3-4 months old calves. The 3rd passage cells were seeded onto fibrin-polyurethane scaffolds (8 mm × 4 mm). Experiment included 5 groups: unloaded culture for 2 weeks (group A), direct load for 2 weeks (group B), unloaded culture for 4 weeks (group C), direct load for 4 weeks (group D), and unload for 2 weeks followed by load for 2 weeks (group E). The cell-scaffold was incubated in incubator (unload) or in a joint-specific bioreactor (load culture). At different time points, the samples were collected for DNA and glycosaminoglycan (GAG) quantification detect; mRNA expressions of chondrogenic marker genes such as collagen type I, collagen type II, Aggrecan, cartilage oligomeric matrix protein (COMP), and superficial zone protein (SZP) were detected by real-time quantitative PCR; and histology observations were done by toluidine blue staining and immunohistochemistry staining. Results No significant difference was found in DNA content, GAG content, and the ratio of GAG to DNA among 5 groups (P gt; 0.05). After load, there was a large number of GAG in the medium, and the GAG significantly increased with time (P lt; 0.05). The mRNA expression of collagen type I showed no significant difference among 5 groups (P gt; 0.05). The mRNA expression of collagen type II in group B was significantly increased when compared with group A (P lt; 0.01), and groups D and E were significantly higher than group C (P lt; 0.01); the mRNA expression of Aggrecan in groups D and E were significantly increased when compared with group C (P lt; 0.01), and group E was significantly higher than group D (P lt; 0.01); the mRNA expression of COMP in group B was significantly increased when compared with group A (P lt; 0.01), and group E was significantly higher than group C (P lt; 0.01); and the mRNA expression of SZP in group E was significantly increased when compared with groups C and D (P lt; 0.05). The toluidine blue staining and immunohistochemistry staining displayed that synthesis and secretion of GAG could be enhanced after load; no intensity changes of collagen type I and collagen type II were observed, but intensity enhancement of Agrrecan was seen in groups D and E. Conclusion Different dynamic loads can promote chondrogenesis of the 3rd passage chondrocytes. Culture by load after unload may be the best culture for chondrogenesis, while the 3rd passage chondrocytes induced by mechanical load hold less capacity of chondrogenesis.
Objective To construct a new type of self-assembling peptide nanofiber scaffolds—RGDmx, and to study the cell compatibility of the new scaffolds and the proliferation and chondrogenic differentiation of precartilaginous stem cells(PSCs) in scaffolds. Methods PSCs were separated and purified from newborn Sprague Dawley rats by magnetic activated cell sorting and indentified by immunohistochemistry and immunofluorescent staining. The RGDmx were constructed by mixing KLD-12 and KLD-12-PRG at volume ratio of 1 ∶ 1. PSCs at passage 3 were seeded into the KLD-12 scaffold (control group) and RGDmx scaffold (experimental group). The proliferation of PSCs in 2 groups were observed with the method of cell counting kit (CCK) -8 after 1, 3, 7, and 14 days after culture. The RGDmx were constructed by mixing KLD-12-PRG and KLD-12 at different volume ratios of 0, 20%, 40%, 60%, 80%, and 100% and the prol iferation of PSCs was also observed. The complete chondrogenic medium (CCM) was used to induce chondrogenic differentiation of PSCs in different scaffolds. The differentiation of PSCs was observed by toluidine blue staining and RT-PCR assay. Results PSCs were separated and purified successfully, which were identified by immunohistochemistry and immunofluorescent staining methods. The results of CCK-8 showed that the absorbance (A) value in the experimental group increased gradually and reached the highest at 7 days; the A value in the experimental group was significantly higher than that in the control group at 7 days and 14 days (P lt; 0.05). Meanwhile, the A value in the RGDmx scaffold with a volume ratio of 40% was significantly higher than those in others (P lt; 0.05). After 14 days of induction culture with CCM, the toluidine blue staining results were positive in 2 groups; the results of RT-PCR showedthat the expression levels of collagen type II and the aggrecan in the experimental group were significantly higher than those in the control group (P lt; 0.05). Conclusion The self-assembling peptide nanofiber scaffold—RGDmx is an ideal scaffold for tissue engineer because it has good cell compatibility and more effective properties of promoting the differentiation of PSCs to chondrocytes.
Objective To establ ish a porcine model of articular full-thickness cartilage defect characterized byremaining cartilage calcified zone on femoral trochlea, so as to provide a considerable and comparative control group forinvestigating repair effects of tissue engineered scaffolds in articular cartilage defects with cartilage calcified zone remaining.Methods The full-thickness cartilage column defects (6 mm in diameter, 0.2-0.5 mm in depth) without damage on calcifiedcartilage zone were made on the femoral trochlea in 9 clean-grade 6-month-old Guizhou mini pigs by standard cartilage-defectmakingsuites. Microscopical observation was performed after modeling. Scanning were made by 3.0T MRI at 4 weeks. Thengeneral observation, stereomicroscope, and histological staining were used to observe cartilage repair. Results All animals wereal ive. No infection of incisions or patellar dislocations occurred; they were able to walk with partial weight-bearing immediatelyafter surgery and could move freely without limp at 1 week. Obvious signal discontinuity in trochlea and subchondral bone couldbe observed in MRI, without deep signal change in defects surrounding. Microscopical observation showed a few repair tissueand petechia at base of the defect with clear boundary. Nearly intact calcified zone of cartilage and zonal collapse of subchondralbone in defects could be observed with stereomicroscope. Under common microscope, no chondrocytes was found in defects,as well as negative staining of fast green-safranin O and alcian blue. Under polarized microscope, the bottom of defects werefilled with a l ittle of fibrous tissue presenting continuous and b l ight-refraction by sirius red staining. Conclusion Theanimal model of articular full-thickness cartilage defect on femoral trochlea by standard cartilage-defect-making suites can beapplied for the research of cartilage disease in early human osteoarthritis and function of calcified cartilage zone in pig.
Objective To explore the preparing methods in vitro and test the cl inical appl icabil ity of implantation in vivo of bone marrow stromal stem cells (BMSCs)-biphasic scaffold to repair defects of cartilage and subchondral bone and tocompare the differences in repaired outcomes of composite, single biphasic scaffold and rabbits themselves. Methods The upper chondral phase and the lower osseous phase of the plugs, using poly-lactic-co-glycol ic acid (PLGA), hydroxyapatite (HA), and other biomaterials, were fused into carrier scaffold, on which collagen type I (Col I) was coated. The surface and inner structure of bi phasic scaffold were observed under scanning electron microscope (SEM). BMSCs was isolated from the bone marrow of tibia and femurs of young New Zealand rabbits using centrifuging and washing, and their morphologies and adherences were observed everyday. Then BMSCs were inoculated on the surface of scaffold to form BMSCs-scaffold composites. Osteochondral defects were surgically created on articular surface of femoral intercondyles of 30 New Zealand rabbits, which were divided into groups A, B and C. In group A, a bi phasic osteochondral composite were implanted into defect, BMSCs and biphasic cyl indrical porous plug of PLGA-HA-Col I in group B, and group C was used as a control without implant. Specimens were harvested to make macroscopic and histological observations at the 1st, 3rd, 6th, and 9th months after operation respectively; meanwhile immunohistological and micro-computed tomography (micro CT) examinations were performed and graded at the 9th month after operation. Results SEM showed an excellent connection of holes in the biphasic scaffold infiltrated by Col I. Optical microscopy and SEM showed a good growth of BMSCs in scaffold without obvious cellular morphological changes and an accumulation in the holes. Macroscopic samples showed a resistant existence of defects of group C within 9 months; the scaffold completely degenerated and chondral-l ike tissue formed on articular surface with partly collapses and irregular defects in group A; and smoother surface without collapses and approach to normal with texture of new regeneration in group B. There were statistically significant differences in macroscopic results (P lt; 0.001), group B was superior to group A, and group C was the worst. The micro CT showed good repairs and reconstruction of subchondral bone, with a acceptable integration with newborn chondral-l ike tissue and host bone in group B. Quantificational analysis of relevantparameters showed no significant differences. Histological results showed inflammations located in defects at the 1st month, new tissue grew into scaffold at the 3rd month; new chondral-l ike tissue crept on the margin of defects and biphasic scaffold degenerated completely at the 6th month, and lots of collagen formed in subchondral bone with major fibrocartilage on chondralarea at the 9th month after surgery in groups A and B. In groups A and B, immunohistological observations were weak positive for Col II and positive for Col I. Conclusion Biphasic scaffold implanted in body can induce and accelerate repair of defects of articular cartilages which are mainly filled with fibrocartilage, especially for subchondral bone. Scaffold combined with BMSCs has the best repairing effects 9 months after implantation.
Objective To explore the effect of tissue engineered cartilage reconstructed by using sodium alginate hydrogel and SIS complex as scaffold material and chondrocyte as seed cell on the repair of full-thickness articular cartilage defects. Methods SIS was prepared by custom-made machine and detergent-enzyme treatment. Full-thickness articularcartilage of loading surface of the humeral head and the femoral condyle obtained from 8 New Zealand white rabbits (2-3weeks old) was used to culture chondrocytes in vitro. Rabbit chondrocytes at passage 4 cultured by conventional multipl ication method were diluted by sodium alginate to (5-7) × 107 cells/mL, and then were coated on SIS to prepare chondrocyte-sodium alginate hydrogel-SIS complex. Forty 6-month-old clean grade New Zealand white rabbits weighing 3.0-3.5 kg were randomized into two groups according to different operative methods (n=20 rabbits per group), and full-thickness cartilage defect model of the unilateral knee joint (right or left) was establ ished in every rabbit. In experimental group, the complex was implanted into the defect layer by layer to construct tissue engineered cartilage, and SIS membrane was coated on the surface to fill the defect completely. While in control group, the cartilage defect was filled by sodium alginate hydrogel and was sutured after being coated with SIS membrane without seeding of chondrocyte. General condition of the rabbits after operation was observed. The rabbits in two groups were killed 1, 3, 5, 7, and 9 months after operation, and underwent gross and histology observation. Results Eight rabbits were excluded due to anesthesia death, wound infection and diarrhea death. Sixteen rabbits per group were included in the experiment, and 3, 3, 3, 3, and 4 rabbits from each group were randomly selected and killed 1, 3, 5, 7, and 9 months after operation, respectively. Gross observation and histology Masson trichrome staining: in the experimental group, SIS on the surface of the implant was fused with the host tissue, and the inferface between them disappeared 1 month after operation; part of the implant was chondrified and the interface between the implant and the host tissue was fused 3 months after operation; the implant turned into fibrocartilage 5 months after operation; fiber arrangement of the cartilage in theimplant was close to that of the host tissue 7 months after operation; cartilage fiber in the implant arranged disorderly andactive cell metabol ism and prol iferation were evident 9 months after operation. While in the control group, no repair of thedefect was observed 9 months after operation. No obvious repair was evident in the defects of the control group within 9months after operation. Histomorphometric evaluation demonstrated that the staining intensity per unit area of the reparative tissue in the defect of the experimental group was significant higher than that of the control group at each time point (P lt; 0.05), the chondrification in the experimental group was increased gradually within 3, 5, and 7 months after operation (P lt; 0.05), and it was decreased 9 months after operation comparing with the value at 7 months after operation (P lt; 0.05). Conclusion Constructed by chondrocyte-sodium alginate hydrogel-SIS in complex with surficial suturing of SIS membrane, the tissue engineered cartilage can in-situ repair cartilage defect, promote the regeneration of cartilage tissue, and is in l ine with physiological repair process of articular cartilage.
To study the effect of the repair of rabbit articular cartilage defects by the composite of chondrogenic induction of autologous MSCs and autologous “two-phase” bone matrix gelatin (BMG). Methods Twentyfour healthy adult New Zealand rabbits weighing 2 to 3 kg were divided into group A, B and C with 8 in each. Autologous MSCsderived from group A were cultured in vitro and observed under inverted phase contrast microscope when enough cells through trypsinization transferring in vitro were obtained. Then the growth curves of 1, 3 and 5 passage culture of MSCs were drawn. The 3rd passage MSCs were induced into chondrogenic differentiation by adding TGF-β1 (10 ng/mL), IGF-1 (10 ng/mL) and vitamin C (50 ng/mL) in vitro. At 8 days after induction, the features of chondrocytes were observed under inverted phase contrast microscope, and immunohistochemical staining and Mallory staining were made. Getting out part of the il ium of group A and B, according to the method of Urist, the “two-phase” BMG was acquired. Chondrogenic induction of autologous MSCs was inoculated into the corresponding BMG to set up a composite of cell-carrier, and then it was observed through scanning electric microscope after 3 days of culture. The model of articular cartilage defects of rabbits was made: in group A, autologous cell-carriers were implanted; in group B, there only existed autologous BMG; in group C, there was nothing. At 8, 12 weeks after operation, the gross, HE staining and immunohistochemical staining were made, and grading scales were evaluated according to Wakitani histological grading method. Results Features of MSCs were as follows: the shape of primary cells was shotspindled and of passage cells was long. As to the growth curves of 1, 3 and 5 passage culture of MSCs, passage cells grew slowly for 3 days after being passaged and went into log-growth during the 3rd and the 7th days and into plateau later, but the 3rd passage cells grew best. Observation of MSCs after chondrogenic induction was performed: the shape of cells was ell iptical and the effect of induction was verified by the positive results of collagen type II, S-100 and Mallory staining. Under scanning electricmicroscope, the structure of BMG was good and cells were observed growing in it well. As far as repair of articular cartilage defects are concerned at 8, 12 weeks after transplantation, the defects in group A were repaired by the hyl ine-l ike tissue and the structures of the cartilage surface and normal cartilage were in integrity, and immunohistochemical staining of collagen type II was positive, while those in group B and C were repaired by the fibrous-l ike tissues and the surfaces were irregular. In Wakitanni histological score, at 8 weeks after operation, group A was (3.50 ± 1.51) points, group B was (10.00 ± 1.41) points and group C was (12.00 ± 0.93) points; at 12 weeks, group A was (1.13 ± 0.99) points, group B was (8.38±1.30) points, and group C was (10.13 ± 1.64) points. At different time points, group A was significantly better than group B and C, showing significant differences (P lt; 0.05). Conclusion Induced autologous MSCs and the composite with autologous “two-phase” BMG have the function to repair articular cartilage defects, and they are better than autologous BMG transplanted only or nothing transplanted.
【Abstract】 Objective To compare the effect of PLGA and collagen sponge combined with rhBMP-2 on repairing ofarticular cartilage defect in rabbits respectively. Methods PLGA and collagen sponge were made into cyl inders which were 4 mm in diameter and 3 mm in thickness, and compounded with rhBMP-2 (0.5 mg). Defect 4 mm in diameter were made in both of femoral condyles of 24 two-month-old New Zealand white rabbits. The defects in right 18 knees were treated with PLGA/rhBMP-2 composites (experimental group 1), and the left 18 knees were treated with collagen sponge/rhBMP-2 composites (experimental group 2), the other 12 knees were left untreated as control group. At 4, 12 and 24 weeks after operation, the animals were sacrificed and the newly formed tissues were observed macroscopically and microscopically, graded histologically and analyzed statistically. Results From the results of macroscopical and microscopical observation, in the experimental group 1, the defects were filled with smooth and translucent cartilage; while in the experimental group 2, the white translucent tissues did notfill the defects completely; and in the two experimental groups, the new cartilage tissues demarcated from the surrounding cartilage,chondrocytes distributed uniformly but without direction; a l ittle fibrous tissue formed in the control group 4 weeks postoperatively. In the experimental group 1, the defects were filled completely with white, smooth and translucent cartilage tissue without clear l imit with normal cartilage; while in the experimental group 2, white translucent tissues formed, the boundary still could be recognized; in the two experimental groups, the thickness was similar to that of the normal cartilage; the cells paralleled to articular surface in the surface layer, but in the deep layer, the cells distributed confusedly, the staining of matrix was positive but a l ittle weak; subchondral bone and tide mark recovered and the new tissue finely incorporated with normal cartilage;however, in the control group, there was a l ittle of discontinuous fibrous tissue, chondrocytes maldistributed in the border andthe bottom of the defects 12 weeks postoperatively. In the experimental group 1, white translucent cartilage tissues formed, the boundary disappeared; in the experimental group 2, the color and the qual ity of new cartilage were similar to those of 12 weeks; in the two experimental groups, the thickness of the new cartilage, which appeared smooth, was similar to that of the normal cartilage, the chondrocytes arranged uniformly but confusedly; the staining of matrix was positive and subchondral bone and tide mark recovered, the new tissue finely incorporated with normal cartilage; in the control group, a layer of discontinuous fibrous tissue formed in the bottom of the defects 24 weeks postoperatively. Results of histological grade showed that there were significantdifference between experimental group (1 and 2) and control group at any time point (P lt; 0.01); the scores of 12 weeks and 24 weeks in experimental group 1 and 2 had a significant difference compared with that of 4 weeks (P lt; 0.01), there was no significant difference between 12 weeks and 24 weeks (P gt; 0.05), and there were no significant difference between the two experimental groups at the same time point (P gt; 0.05). Conclusion Both PLGA and collagen sponge as a carrier compounded with rhBMP-2 can repair articular cartilage defects.
Objective To repair the defects in articular cartilage with collagen complex gradient TCP in vivo andto study the regenerated cartilage histomorphologically. Methods The models of defects in articular cartilage were madeartificially in both condylus lateral is femoris of mature rabbits, male or female, with the weight of 2.0-2.5 kg. The right defects were implanted with the material of Col/TCP as the experimental group and the left defects were untreated as the control group. The rabbits were killed at 4, 6, 8, 12 and 24 weeks after operation, respectively, with 6 ones at each time, and the macroscopic, histological, ultrastructural examinations and semi-quantity cartilage scoring employing Wakitanifa repaired cartilage value system were performed. Results Four weeks after operation, the defects in the experimental group were partly filled with hyal ine cartilage. Twelve weeks after operation, the defects in the experimental group were completely filled with mature hyal ine cartilage. Twenty-four weeks after operation, regenerated cartilage had no ataplasia. However, fibrous tissues were seen in the control group all the time. At 4, 6, 8, 12 and 24 weeks ostoperatively, the Wakitanifa cartilage scores were 7.60 ± 0.98, 5.69 ± 0.58, 4.46 ± 0.85, 4.35 ± 0.12 and 4.41 ± 0.58, respectively, in the experimental group and 10.25 ± 1.05, 9.04 ± 0.96, 8.96 ± 0.88, 8.88 ± 0.68 and 8.66 ± 0.54, respectively, in the control group. At 4, 6, 8, 12 and 24 weeks postoperatively, the collagen II contents were 0.28% ± 0.01%, 0.59% ± 0.03%, 0.68% ± 0.02%, 0.89% ± 0.02% and 0.90% ± 0.01%, respectively, in the experimental group, while 0.08% ± 0.02%, 0.09% ± 0.04%, 0.11% ± 0.03%, 0.25% ± 0.03% and 0.29% ± 0.01%, respectively, in the control group. Differences between the control group and the experimental group were significant (P lt; 0.05). By then, typical chondrocyte was observed by transmission electron microscope in the experimental group and much fiber with less fibrocyte was observed in the control group. Conclusion Three-dimensional scaffold collagen complex gradient TCP may induce cartilage regeneration to repair the defects of articular cartilage in vivo.