Objective To prepare collagen-chitosan /nano-hydroxyapatite-collagen-polylactic acid (Col-CS/ nHAC-PLA) biomimetic scaffold and to examine its biocompatibility so as to lay the foundation for its application on the treatment of osteochondral defect. Methods PLA was dissolved in dioxane for getting final concentration of 8%, and the nHAC power was added at a weight ratio of nHAC to PLA, 1 ∶ 1. The solution was poured into a mold and frozen. CS and Col were dissolved in 2% acetum for getting the final concentrations of 2% and 1% respectively, then compounded at a weight ratio of CS to Col, 20 ∶ 1. The solution was poured into the frozen mold containing nHAC-PLA, and then biomimetic osteochondral scaffold of Col-CS/nHAC-PLA was prepared by freeze-drying. Acute systemic toxicity test, intracutaneous stimulation test, pyrogen test, hemolysis test, cytotoxicity test, and bone implant test were performed to evaluate its biocompatibility. Results Col-CS/nHAC-PLA had no acute systemic toxicity. Primary irritation index was 0, indicating that Col-CS/nHAC-PLA had very slight skin irritation. In pyrogen test, the increasing temperature of each rabbit was less than 0.6℃, and the increasing temperature sum of 3 rabbits was less than 1.3℃, which was consistent with the evaluation criteria. Hemolytic rate of Col-CS/nHAC-PLA was 1.38% (far less than 5%). The toxicity grade of Col-CS/nHAC-PLA was classified as grade I. Bone implant test showed that Col-CS/nHAC-PLA had good biocompatibility with the surrounding tissue. Conclusion Col-CS/ nHAC-PLA scaffold has good biocompatibility, which can be used as an alternative osteochondral scaffold.
ObjectiveTo explore a method of three-dimensional (3D) printing technology for preparation of personalized rat brain tissue cavity scaffolds so as to lay the foundation for the repair of traumatic brain injury (TBI) with tissue engineered customized cavity scaffolds. MethodsFive male Sprague Dawley rats[weighing (300±10) g] were induced to TBI models by electric controlled cortical impactor. Mimics software was used to reconstruct the surface profile of the damaged cavity based on the MRI data, computer aided design to construct the internal structure. Then collagen-chitosan composite was prepared for 3D bioprinter of bionic brain cavity scaffold. ResultsMRI scans showed the changes of brain tissue injury in the injured side, and the position of the cavity was limited to the right side of the rat brain cortex. The 3D model of personalized cavity containing the internal structure was successfully constructed, and cavity scaffolds were prepared by 3D printing technology. The external contour of cavity scaffolds was similar to that of the injured zone in the rat TBI; the inner positive crossing structure arranged in order, and the pore connectivity was good. ConclusionCombined with 3D reconstruction based on MRI data, the appearance of cavity scaffolds by 3D printing technology is similar to that of injured cavity of rat brain tissue, and internal positive cross structure can simulate the topological structure of the extracellular matrix, and printing materials are collagen-chitosan complexes having good biocompatibility, so it will provide a new method for customized cavity scaffolds to repair brain tissue cavity after TBI.