Focusing on the poor mechanical strength of porous bioceramics bone scaffold, and taking into account of the good mechanical properties of biodegradable magnesium alloy, we proposed a novel method to fabricate magnesium alloy/bioceramics composite bone scaffold with stereolithography double channels. Firstly, a scaffold structure without mutually connected double channels was designed. Then, an optimized bioceramics scaffold was fabricated according to stereolithography and gel-casing. Molten AZ31 magnesium alloy was perfused into the secondary channel of scaffold by low-pressure casting, and magnesium alloy/bioceramics composite bone scaffold was obtained when magnesium alloy was solidified. The compression test showed that the strength of bioceramics scaffold with only one channel and without magnesium alloy was (9.76±0.64) MPa, while the strength of magnesium alloy/bioceramics composite scaffold with double channels was (17.25±0.88) MPa. It can be concluded that the magnesium alloy/bioceramics composite is obviously able to improve the scaffold strength.
ObjectiveTo improve the poor mechanical strength of porous ceramic scaffold, an integrated method based on three-dimensional (3-D) printing technique is developed to incorporate the controlled double-channel porous structure into the polylactic acid/β-tricalcium phosphate (PLA/β-TCP) reinforced composite scaffolds (double-channel composite scaffold) to improve their tissue regeneration capability and the mechanical properties. MethodsThe designed double-channel structure inside the ceramic scaffold consisted of both primary and secondary micropipes, which parallel but un-connected. The set of primary channels was used for cell ingrowth, while the set of secondary channels was used for the PLA perfusion. Integration technology of 3-D printing technique and gel-casting was firstly used to fabricate the double-channel ceramic scaffolds. PLA/β-TCP composite scaffolds were obtained by the polymer gravity perfusion process to pour PLA solution into the double-channel ceramic scaffolds through the secondary channel set. Microscope, porosity, and mechanical experiments for the standard samples were used to evaluate the composite properties. The ceramic scaffold with only the primary channel (single-channel scaffold) was also prepared as a control. ResultsMorphology observation results showed that there was no PLA inside the primary channels of the double-channel composite scaffolds but a dense interface layer between PLA and β-TCP obviously formed on the inner wall of the secondary channels by the PLA penetration during the perfusion process. Finite element simulation found that the compressive strength of the double-channel composite scaffold was less than that of the single-channel scaffold; however, mechanical tests found that the maximum compressive strength of the double-channel composite scaffold[(21.25±1.15) MPa] was higher than that of the single-channel scaffold[(9.76±0.64) MPa]. ConclusionThe double-channel composite scaffolds fabricated by 3-D printing technique have controlled complex micropipes and can significantly enhance mechanical properties, which is a promising strategy to solve the contradiction of strength and high-porosity of the ceramic scaffolds for the bone tissue engineering application.