Objective To give a prel iminary experimental evidence and to prove chitosan and allogeneic morsel ized bone as potential bone substitutions in repairing rabbit radius segmental defect. Methods Chitosan and allogeneic morsel ized bone were mixed with various ratios (1 ∶ 5, 1 ∶ 10, 1 ∶ 25, 1 ∶ 50, and 1 ∶ 100). After preparation, the physicaland chemical properties of the composites were prel iminary detected; the composites at the ratios of 1 ∶ 50 and 1 ∶ 25 had good physical and chemical properties and were used for the animal experiment. The radius segmental defects of 15 mm in length were made in 50 adult New Zealand white rabbits (weighing 2.5-3.0 kg), then the animals were divided into 2 groups. In groups A and B, chitosan/allogeneic morsel ized bone composites were implanted at the ratio of 1 ∶ 50 and 1 ∶ 25, respectively. After 1, 2, 4, 8, and 12 weeks of operation, the gross, histological, immunohistochemical observations were performed. Before the rabbits were sacrified, X-ray films were taken; the serum calcium and alkal ine phosphatase (ALP) concentration were measured; and the biomechanical measurement was carried out at 12 weeks. Results The results of gross observation were essentially consistent with those of the X-ray films. The histological observation showed that the bone formation was earl ier in group A than in group B; the amount of new bone formation in group A was more than that in group B; and the bone forming area in group A was bigger than that in group B (P lt; 0.05) at 4 and 8 weeks after operation. The immunohistochemical staining showed that vascular endothel ial growth factor and insul in-l ike growth factor receptor II proteins expressed in the cytoplasm of 2 groups after 4 and 8 weeks, and the expression in group A was higher than that in group B (P lt; 0.05). There was no significant difference in the serum calcium concentration between 2 groups at each time point (P gt; 0.05). After 4 and 8 weeks, the ALP concentration in group A was significantly higher than that in group B (P lt; 0.05). After 12 weeks, the radius maximum bending loads of groups A and B were (299.75 ± 27.69) N and (278.54 ± 17.09) N, respectively, showing significant difference (t=4.045,P=0.002). Conclusion The composite of chitosan and allogeneic morsel ized bone has good osteogeneic activity and can beused as a bone tissue engineering scaffold, and the optimum ratio of chitosan to allogeneic morsel ized bone was 1 ∶ 50.
Objective To review the recent research and clinical progress of artificial osteoconductive materials. Methods Recent and related literatures were extensively and comprehensively reviewed. Results Many achievements about the clinical application of the artificial osteoconductive materials were made. Ithad become one of the hotspots of bone tissue engineering research. Some were clinically applied and good clinical results were achieved. Conclusion As it provides new clinic method for treating bone defect, artificial osteoconductive material is of great potential in its application. To improve its microstructure, macroshape, mechanism of osteoinductive ability, and to accelerate new bone for mation will be the hotspots of the research on artificial osteoconductive material.
Abstract To investigate the ectopic new bone formation following implantation of bovine hydroxyapatite Bio-oss together with free periosteum, 12 chabb: ch rabbits were selected. In 10 rabbits, Bio-oss block together with free periosteum was implanted in the gastrocnemius muscle of one leg randomly, and Bio-oss block alone was implanted in the same muscle of the other leg. In the other 2 rabbits, the periosteum was implanted into the gastrocnemius musle of both legs. Histologic examination and quantitative analysis of newbone formation were performed at 3 and 6 weeks postoperatively. The results showed that in the legs implanted bovine hydroxyapatite Bio-oss together with freeperiosteum, new bone formation began at 5th day after implantation. The area ofnew bone composed of 19.0% of the specimens at 3 weeks postoperatively. No boneformation through out the experimental period in Bio-oss block alone implantedlegs and also periosteum implanted legs. We concluded that bovine hydroxyapatite Bio-oss has a good capacity of osteoconduction. New bone can be formed after the implantation of hydroxyapatite combined with free periosteum.