Objective To evaluate the feasibility of poly-L-lactide(PLLA)/porcinederived xenogeneic bone(PDXB) composite as a scaffold for the bone tissue engineering. Methods The film and the scaffold of the PLLA-PDXB composite were respectively prepared by a solution casting method and a solution casting-particle leaching method. The composite film and scaffold were further treated by the surface alkaline hydrolysis. The surface morphology of the composite was observed by the scanning electron microscopy, and hydrophilicity degree of the composite was measured. The OCT-1 osteoblastlike cells were cultured and amplified in vitro as the seeding cells, which werethen implanted on the film and scaffold. The adherence rate, adherence shape,proliferating activity, and growing morphology of the OCT-1 osteoblastlikecells were observed on the film. Results The PDXB particle 50 μm in diameter on average had a similar phase structure to that of hydroxyapatite. But its Ca/P ratio was lower than that of hydroxyapatite. After the surface alkaline hydrolysis, the PDXB particle could be exposed on the surface of the PLLA-PDXB composite. The surface roughness and hydrophilicity of the PLLAPDXB composite were obviously enhanced. The cell adherence rate and the cell proliferation activity of the PLLAPDXB composite were higher than those of the pure PLLA material. The cells tended to grow on the exposed surface of the PDXB particles. The cells seeded on the composite scaffold could migrate to the inside of the composite scaffold and grew well. Conclusion The PLLA-PDXB composite has a good cell affinity, and this kind of composite can hopefullybecome a new scaffold material to be used in the bone tissue engineering.
ObjectiveTo investigate the effects of micro/nano-structure and antimicrobial peptides (AMPs) on antibacterial properties of titanium (Ti) metallic surface.MethodsTi disks were treated via sandblasted large-grit acid-etched (SLA) and alkali-heat treatment (AHT) to build the micro/nano-structure, on which AMPs were spin-coated with a certain amount (10, 30, 50, 70, and 90 μg). Scanning electron microscope (SEM) and energy dispersive spectroscopy (EDS) were used to observe the surface structure and characterize the surface elements (i.e. contents of C, N, O, and Ti). Ti disks loaded with AMPs of difference amounts were co-cultured with Staphylococcus aureus (S. aureus) for 24 hours. After that, the formation and dimension of antibacterial circle were measured. Furthermore, the Ti disks treated with different approaches (untreated, SLA treatment, SLA+THA treatment, and 90 μg AMPs-loaded samples) were co-cultured with S. aureus and Escherichia coli (E.coli) for 3 hours, bacterial adhesion on the disks were evaluated by using SEM. The antibacterial performances in solution were quantitatively evaluated by immersing the Ti disks in bacterial solutions and measuring the absorbance (A) values.ResultsIt was found that the nanoporous structure could be easily constructed by SLA+AHT approach. After spin-coating AMPs, the nanopores with the diameter less than 200 nm were almost covered. According to the element analysis, with the increase of AMPs, the C content gradually increased; the N content was not detected until AMPs amount reached 70 μg on the disks. The diameter of antibacterial circle clearly depended on the AMPs amount. The Ti disks loaded with 90 μg AMPs had significantly larger antibacterial circles than the other Ti disks (P<0.05). Based on the SEM observation, the Ti disks loaded with 90 μg AMPs has the least bacterial attachment compared with the other Ti disks (P<0.05). TheA value of bacterial solution immersed with the Ti disks loaded with 90 μg AMPs was much lower than the other Ti disks (P<0.05).ConclusionThe approach of micro/nano-structure and AMPs can improve the antibacterial properties of Ti metallic surface.