Objective To fabricate a novel composite scaffold with acellular demineralized bone matrix/acellular nucleus pulposus matrix and to verify the feasibility of using it as a scaffold for intervertebral disc tissue engineering through detecting physical and chemical properties. Methods Pig proximal femoral cancellous bone rings (10 mm in external diameter, 5 mm in internal diameter, and 3 mm in thickness) were fabricated, and were dealed with degreasing, decalcification, and decellularization to prepare the annulus fibrosus phase of scaffold. Nucleus pulposus was taken from pig tails, decellularized with Triton X-100 and deoxycholic acid, crushed and centrifugalized to prepare nucleus pulposus extracellular mtrtix which was injected into the center of annulus fibrosus phase. Then the composite scaffold was freeze-dryed, cross-linked with ultraviolet radiation/carbodiimide and disinfected for use. The scaffold was investigated by general observation, HE staining, and scanning electron microscopy, as well as porosity measurement, water absorption rate, and compressive elastic modulus. Adipose-derived stem cells (ADSCs) were cultured with different concentrations of scaffold extract (25%, 50%, and 100%) to assess cytotoxicity of the scaffold. The cell viability of ADSCs seeded on the scaffold was detected by Live/Dead staining. Results The scaffold was white by general observation. The HE staining revealed that there was no cell fragments on the scaffold, and the dye homogeneously distributed. The scanning electron microscopy showed that the pore of the annulus fibrosus phase interconnected and the pore size was uniform; acellular nucleus pulposus matrix microfilament interconnected forming a uniform network structure, and the junction of the scaffold was closely connected. The novel porous scaffold had a good pore interconnectivity with (343.00 ± 88.25) µm pore diameter of the annulus fibrosus phase, 82.98% ± 7.02% porosity and 621.53% ± 53.31% water absorption rate. The biomechanical test showed that the compressive modulus of elasticity was (89.07 ± 8.73) kPa. The MTT test indicated that scaffold extract had no influence on cell proliferation. Live/Dead staining showed that ADSCs had a good proliferation on the scaffold and there was no dead cell. Conclusion Novel composite scaffold made of acellular demineralized bone matrix/acellular nucleus pulposus matrix has good pore diameter and porosity, biomechanical properties close to natural intervertebral disc, non-toxicity, and good biocompatibility, so it is a suitable scaffold for intervertebral disc tissue engineering.
Objective To evaluate the influence of PKH26 labeling on the biological function of the goat nucleus pulposus cells and the biological function of seeded cells in nude mice by in vivo imaging techonology. Methods Primary nucleus pulposus cells were isolated by enzymatic digestion from the nucleus pulposus tissue of the 1-year-old goat disc. The nucleus pulposus cells at passage 1 were labeled with PKH26 and the fluorescent intensity was observed under the fluorescence microscopy. The labeled cells were stained with toluidine blue and collagen type II immunocytochemistry. The cells viability and proliferation characteristics were assessed by trypan blue staining and MTT assay, respectively. Real-time fluorescent quantitative PCR was used to detect the gene expressions of collagen types I and II, and aggrecan. The fluorescent intensity and scope of the nucleus pulposus cells-scaffold composite in vivo for 6 weeks after implanting into 5 6-week-old male nude mice were measured by in vivo imaging technology. Results Primary nucleus pulposus cells were ovoid in cell shape, showing cluster growth, and the cells at passage 1 showed chondrocyte-like morphology under the inverted phase contrast microscope. The results of toluidine blue and collagen type II immunocytochemistry staining for nucleus pulposus cells at passage 1 were positive. The fluorescent intensity was even after labeling, and the cell viability was more than 95% before and after PKH26 labeling. There was no significant difference in cell growth curve between before and after labeling (P gt; 0.05). The real-time fluorescent quantitative PCR showed that there was no significant difference in gene expressions of collagen types I and II, and aggrecan between before and after labeling (P gt; 0.05). Strong fluorescence in nucleus pulposus cells-scaffold composite was detected and by in vivo imaging technology. Conclusion The PKH26 labeling has no effect on the activity, proliferation, and cell phenotype gene expression of the nucleus pulposus cells. A combination of PKH26 labeling and in vivo imaging technology can track the biological behavior of the cells in vivo.
Objective To observe the chondrogenic differentiation of adipose-derived stem cells (ADSCs) by co-culturing chondrocytes and ADSCs. Methods ADSCs and chondrocytes were isolated and cultured from 8 healthy 4-month-old New Zealand rabbits (male or female, weighing 2.2-2.7 kg). ADSCs and chondrocytes at passage 2 were used. The 1 mL chondrocytes at concentration 2 × 104/mL and 1 mL ADSCs at concentration 2 × 104/mL were seeded on the upper layer and lower layer of Transwell 6-well plates separately in the experimental group, while ADSCs were cultured alone in the control group. The morphology changes of the induced ADSCs were observed by inverted phase contrast microscope. The glycosaminoglycan and collagen type II synthesized by the induced ADSCs were detected with toluidine blue staining and immunohistochemistry staining. The mRNA expressions of collagen type II, aggrecan, and SOX9 were detected with real-time fluorescent quantitative PCR. Results ADSCs in the experimental group gradually became chondrocytes-like in morphology and manifested as round; while ADSCs in the control group manifested as long spindle in morphology with whirlool growth pattern. At 14 days after co-culturing, the results of toluidine blue staining and immunohistochemistry staining were positive in the experimental group, while the results were negative in the control group. The results of real-time fluorescent quantitative PCR indicated that the expression levels of collagen type II, aggrecan, and SOX9 mRNA in the experimental group (1.43 ± 0.07, 2.13 ± 0.08, and 1.08 ± 0.08) were significantly higher than those in the control group (0.04 ± 0.03, 0.13 ± 0.04, and 0.10 ± 0.02) (P lt; 0.05). Conclusion ADSCs can differentiate into chondrocytes-like after co-culturing with chondrocytes.
Objective To observe the histological structure and cytocompatibility of novel acellular bone matrix (ACBM) and to investigate the feasibility as a scaffold for bone tissue engineering. Methods Cancellous bone columns were harvested from the density region of 18-24 months old male canine femoral head, then were dealt with high-pressure water washing, degreasing, and decellularization with Trixon X-100 and sodium deoxycholate to prepare the ACBM scaffold. The scaffolds were observed by scanning electron microscope (SEM); HE staining, Hoechst 33258 staining, and sirius red staining were used for histological analysis. Bone marrow mesenchymal stem cells (BMSCs) from canine were isolated and cultured with density gradient centrifugation; the 3rd passage BMSCs were seeded onto the scaffold. MTT test was done to assess the cytotoxicity of the scaffolds. The proliferation and differentiation of the cells on the scaffold were observed by inverted microscope, SEM, and live/dead cell staining method. Results HE staining and Hoechst 33258 staining showed that there was no cell fragments in the scaffolds; sirius red staining showed that the ACBM scaffold was stained crimson or red and yellow alternating. SEM observation revealed a three dimensional interconnected porous structure, which was the microstructure of normal cancellous bone. Cytotoxicity testing with MTT revealed no significant difference in absorbance (A) values between different extracts (25%, 50%, and 100%) and H-DMEM culture media (P gt; 0.05), indicating no cytotoxic effect of the scaffold on BMSCs. Inverted microscope, SEM, and histological analysis showed that three dimensional interconnected porous structure of the scaffold supported the proliferation and attachment of BMSCs, which secreted abundant extracellular matrices. Live/dead cell staining results of cell-scaffold composites revealed that the cells displaying green fluorescence were observed. Conclusion Novel ACBM scaffold can be used as an alternative cell-carrier for bone tissue engineering because of thoroughly decellularization, good mircostructure, non-toxicity, and good cytocompatibility.