Objective To construct a new type of self-assembling peptide nanofiber scaffolds—RGDmx, and to study the cell compatibility of the new scaffolds and the proliferation and chondrogenic differentiation of precartilaginous stem cells(PSCs) in scaffolds. Methods PSCs were separated and purified from newborn Sprague Dawley rats by magnetic activated cell sorting and indentified by immunohistochemistry and immunofluorescent staining. The RGDmx were constructed by mixing KLD-12 and KLD-12-PRG at volume ratio of 1 ∶ 1. PSCs at passage 3 were seeded into the KLD-12 scaffold (control group) and RGDmx scaffold (experimental group). The proliferation of PSCs in 2 groups were observed with the method of cell counting kit (CCK) -8 after 1, 3, 7, and 14 days after culture. The RGDmx were constructed by mixing KLD-12-PRG and KLD-12 at different volume ratios of 0, 20%, 40%, 60%, 80%, and 100% and the prol iferation of PSCs was also observed. The complete chondrogenic medium (CCM) was used to induce chondrogenic differentiation of PSCs in different scaffolds. The differentiation of PSCs was observed by toluidine blue staining and RT-PCR assay. Results PSCs were separated and purified successfully, which were identified by immunohistochemistry and immunofluorescent staining methods. The results of CCK-8 showed that the absorbance (A) value in the experimental group increased gradually and reached the highest at 7 days; the A value in the experimental group was significantly higher than that in the control group at 7 days and 14 days (P lt; 0.05). Meanwhile, the A value in the RGDmx scaffold with a volume ratio of 40% was significantly higher than those in others (P lt; 0.05). After 14 days of induction culture with CCM, the toluidine blue staining results were positive in 2 groups; the results of RT-PCR showedthat the expression levels of collagen type II and the aggrecan in the experimental group were significantly higher than those in the control group (P lt; 0.05). Conclusion The self-assembling peptide nanofiber scaffold—RGDmx is an ideal scaffold for tissue engineer because it has good cell compatibility and more effective properties of promoting the differentiation of PSCs to chondrocytes.
ObjectiveTo investigate the effects of micro-fracture and insul in-l ike growth factor 1 (IGF-1) in treatment of articular cartilage defect in rabbits. MethodsTwenty-four New Zealand white rabbits (aged, 4-6 months; weighing, 2.5-3.5 kg) were randomly divided into 4 groups (n=6):micro-fractures and recombinant human IGF-1 (rhIGF-1) treatment group (group A), micro-fracture control group (group B), rhIGF-1 treatment control group (group C), and blank control group (group D). Full thickness articular cartilage defects of 8 mm×6 mm in size were created in the bilateral femoral condyles of all rabbits. The micro-fracture surgery was performed in groups A and B. The 0.1 mL rhIGF-1 (0.01 μg/μL) was injected into the knee cavity in groups A and C at 3 times a week for 4 weeks after operation, while 0.1 mL sal ine was injected in groups B and D at the same time points. At 4, 12, and 24 weeks, the gross, histological, and immunohistochemical observations were performed, and histological score also was processed according to Wakitani's score criteria. The collagen contents in the repair tissues and normal patellofemoral cartilage were detected by the improved hydroxyproline (HPR) method at 24 weeks. Electron microscope was used to observe repair tissues of groups A and B at 24 weeks. Results All animals were survival at the end of experiment. At 24 weeks after operation, defect was repaired with time, and the repair tissue was similar to normal cartilage in group A; the repair tissue was even without boundary with normal cartilage in group B; and the repair tissue was uneven with clear boundary with normal cartilage in groups C and D. Histological staining showed that the repair tissues had no difference with normal cartilage in group A; many oval chondrocytes-l ike cells and l ight-colored matrix were seen in the repair tissues of group B; only a few small spindle-shaped fibroblasts were seen in groups C and D. Moreover, histological scores of group A were significantly better than those of groups B, C, and D (P<0.05) at 4, 12, and 24 weeks. Electron microscope observation showed that a large number of lacuna were seen on the surface of repair tissue in group A, and chondrocytes contained glycogen granules were located in lacunae, and were surrounded with the collagen fibers, which was better than that in group B. Collagen content of the repair tissue in group A was significantly higher than that in groups B, C, and D (P<0.05), but it was significantly lower than that of normal cartilage (P<0.05). Conclusion Combination of micro-fracture and rhIGF-1 for the treatment of full thickness articular cartilage defects could promote the repair of defects by hyaline cartilage.