Objective To research the effect of porcine acellular dermal matrix in the reconstruction of abdominal wall defects in rabbits, and to investigate the appl ication feasibil ity of xeno-transplantation of acellular dermal matrix. Methods The porcine acellular dermal matrix was prepared from a health white pig. Twenty-six Japanese white rabbits (weighing 2.2-2.3 kg, female or male) were randomly assigned to 2 groups: the control group (n=6) and the experimental group (n=20). In the control group, the full-thickness abdominal wall defect of 5.0 cm × 0.5 cm was made, and the defect wassutured directly; in the experimental group, the full-thickness abdominal wall defect of 5.0 cm × 2.5 cm was made, and the defect was repaired with porcine acellular dermal matrix patch at the same size as the defect. At 5 weeks after surgery, the incidence of hernia and the intra-abdominal adhesions were observed and the wound breaking strength was compared between the patchfascia interface and the fascia-fascia interface. The graft vascularization was evaluated through histological analysis at 6 months after surgery in the experimental group. Results No hernia occurred in all rabbits of 2 groups. At 5 weeks after surgery, heal ing was observed between patch and the muscularfascia; the vascularization was seen in the porcine acellular dermal matrix patch. There was no significant difference in the adhesion grade (Z= —0.798, P=0.425) between the experimental group (grade 2 in 1 rabbit, grade 1 in 5, and grade 0 in 12) and the control group (grade 1 in 1 and grade 0 in 5). No significant difference was found (t= —0.410, P=0.683) in the breaking strength between the patch-fascia interface in the experimental group [(13.0 ± 5.5) N] and the fascia-fascia interface in control group [(13.6 ± 4.0) N]. In the experimental group, the small vessels and the infiltration of inflammatory cells were observed in the porcine acellular dermal matrix patch after 5 weeks through histological observations. The junctions of the patch-fascia interface healed with fibrous connective tissue. At 6 months after surgery, the inflammation was subsided and the collagen fiber of the patch was reconstructed. Conclusion The porcine acellular dermal matrix patchhas good results in repairing full-thickness abdominal wall defect. The patch-fascia interface has siml iar breaking strength to the fascia-fascia interface. The collagen fibers of the patch are reconstructed.
ObjectiveTo investigate the histological changes and vascularization of the porcine acellular dermal matrix (P-ADM) processed with matrix metalloproteinase 7 (MMP-7) (P-ADM-pm) after implanted into rats. MethodsSixty-two pieces of porcine reticular layer dermis which were from the pig abdominal skin and obtained by using a mechanical method, were randomly divided into group A (n=31) and group B (n=31). The porcine reticular layer dermis in 2 groups were treated with decellularization (P-ADM), then the P-ADM in group B were treated with processing by MMP-7 (P-ADM-pm). Thirty adult male Wistar rats were selected. P-ADM (group A) and P-ADM-pm (group B) were subcutaneously transplanted into the left and right fascia lacuna, respectively. The implants were harvested from 6 rats at 3, 7, 14, 21, and 28 days after implantation, respectively. Gross, histochemical, and immunohistochemical observations, and scanning electron microscopy (SEM) examination were performed to observe host cells, microvessels infiltration and histological changes in the implants. ResultsNo rat died in the experiment, incision healed well and no obvious inflammatory reaction was seen in all rats. Gross observation suggested that the implants of 2 groups were encapsulated by a thin layer of connective tissue at 7 days after implantation. With the time of implantation, the microvessels increased and coarsened, and the changes of group B were more obvious than those of group A. At 21 days, the microvessels of 2 groups decreased, and the implants of group B showed complete vascularization. The histochemical and immunohistochemical observations showed that group A had more severe inflammatory response than group B. Fibroblasts and microvessels in group B appeared in the superficial zone of implant at 3 and 7 days after implantation and they could be observed in the center zone of implant at 14 and 21 days. However, fibroblasts and microvessels in group A appeared in the superficial zone of implant at 3 and 14 days and they could not be observed in the center zone of implant at 28 days. Fibroblasts and microvessels of group B were significantly more than those of group A (P < 0.05). SEM examination showed that more fibroblasts and new collagen fibrils were observed in group B at 14 days. ConclusionThe host response to P-ADM-pm is similar to normal wound healing, and P-ADM-pm as implantable scaffold material plays a good template conduction role.