Objective To observe the release pattern of the microcysts and the effect of ectopic osteogenesis of combined micromorselized bone by optimized preparation of microcysts. Methods Optimized poly-DLlactide-co-glycolide (PLGA) microcysts manufacturing method was performed with the orthogonal design, and the accumulated release amount of microcysts was calculated at 2 h, 4 h, 8 h, 12 h, 24 h, 36 h, 48 h, 60 h, 72 h, 84 h, 96 h, 120 h, 144 h, 168 h, 192 h, 216 h, 240 h and 264 h. Twentyfour Wistar rats were divided into 4 groups (n=6) and 1 cm length incision was cut in their bilateral thighs skin, forming 48 gluteus maximus muscle sackmodels. In group A,collagen was implanted to bilateral muscle sacks respectively. In group B, collagen and autologous morselized bone were implanted to bilateral muscle sacks. Ingroup C, collagen and rhBMP-2/PLGA delayed release microcysts were implanted to bilateralmuscle sacks respectively. In group D, collagen and morselized bone/rhBMP-2/PLGA delayed release microcysts were implanted to bilateral muscle sacks. Gross and histologic observations were made at 3, 4 and 5 weeks postoperatively.Results Every optimized variance had an effect on particle diameter of microcyst and its encapsulating rate. The microcyst’s surface was smooth and had a fine spheroplast, which released slowly within 11 days in vitro. In thethird week postoperatively, the graft in group A could not be touched, while the graft in all other 3 groups was still found. After 3 weeks, collagen was absorbed completely in group A, the residual collagen could be seen in groups B, C andD. After 4 weeks, collagen could be seen in group A; micromorselized bone continued to be absorbed and became smaller in group B; microsphere became smaller, osteoblasts increased in group C; micromorselized bone and microsphere continuedto be absorbed, oteoblasts and chondroblasts increased. After 5 weeks, implantsbecame small, microsphere was absorbed, osteoblasts and chondroblasts became more in groups B, C and D. Microcysts presented with white granuloshape and were packaged in tissue pieces. Histologic observation showed that the PLGA microcysts in 3 weeks and 4 weeks could be absorbed gradually as the time in vivo, if combining with morselzed bone they could produce abundant induced osteoblasts and chondroblasts. Conclusion Optimizing the preparation technology of microcysts has delayed their release during a long period in vitro. Autologous micromorselized bone can be ectopicly induced to produce large amount of osteoblasts in gluteus maximus muscle sack, where PLGA microcysts can combine organically and bring about the bone formation with less amount of growth factors.
ObjectiveTo evaluate the effect of a novel micro-arc oxidation (MAO) coated magnesium-zinc-calcium (Mg-Zn-Ca) alloy scaffold/autologous bone particles to repair critical size bone defect (CSD) in rabbit and explore the novel scaffold in vivo corrosion resistance and biocompatibility.MethodsSeventy-two New Zealand white rabbits were randomly divided into 3 groups (n=24), group A was uncoated Mg-Zn-Ca alloy scaffold group, group B was 10 μm MAO coated Mg-Zn-Ca alloy scaffold group, and group C was control group with only autologous bone graft. The animals were operated to obtain bilateral ulnar CSD (15 mm in length) models. The bone fragment was removed and minced into small particles and were filled into the scaffolds of groups A and B. Then, the scaffolds or autologous bone particles were replanted into the defects. The animals were sacrificed at 2, 4, 8, and 12 weeks after surgery (6 rabbits each group). The local subcutaneous pneumatosis was observed and recorded. The ulna defect healing was evaluated by X-ray image and Van Gieson staining. The X-ray images were assessed and scored by Lane-Sandhu criteria. The percentage of the lost volume of the scaffold (ΔV) and corrosion rate (CR) were calculated by the Micro-CT. The Mg2+ and Ca2+ concentrations were monitored during experiment and the rabbit liver, brain, kidney, and spleen were obtained to process HE staining at 12 weeks after surgery.ResultsThe local subcutaneous pneumatosis in group B was less than that in group A at 2, 4, and 8 weeks after surgery, showing significant differences between 2 groups at 2 and 4 weeks after surgery (P<0.05); and the local subcutaneous pneumatosis was significantly higher in group B than that in group A at 12 weeks after surgery (P<0.05). The X-ray result showed that the score of group C was significantly higher than those of groups A and B at 4 and 8 weeks after surgery (P<0.05), and the score of group B was significantly higher than that of group A at 8 weeks (P<0.05). At 12 weeks after surgery, the scores of groups B and C were significantly higher than that of group A (P<0.05). Meanwhile, the renew bone moulding of group B was better than that in group A at 12 weeks after surgery. Micro-CT showed that ΔV and CR in group B were significantly lower than those in group A (P<0.05). Van Gieson staining showed that group B had better biocompatibility and osteanagenesis than group A. The Mg2+ and Ca2+ concentrations in serum showed no significant difference between groups during experiments (P>0.05). And there was no obvious pathological changes in the liver, brain, kidney, and spleen of the 3 groups with HE staining at 12 weeks.ConclusionThe MAO coated Mg-Zn-Ca alloy scaffold/autologous bone particles could be used to repair CSD effectively. At the same time, 10 μm MAO coating can effectively improve the osteanagenesis, corrosion resistance, and biocompatibility of Mg-Zn-Ca alloy scaffold.