The present study is aimed to investigate the early clinical effects of nano-hydroxyapatite/polyamide 66 intervertebral fusion cage (n-HA/PA66 cage) for the treatment of lumbar degenerative diseases. We selected 27 patients with lumbar degenerative diseases who were managed by posterior decompression or reset operation combined with n-HA/PA66 cage intervertebral fusion and internal fixation from August 2010 to January 2012. The oswestry disability index (ODI), low back and leg pain visual analogue score (VAS), and intervertebral height (IH) were evaluated at preoperation, 1 week postoperation and the last follow-up period, respectively. Intervertebral bony fusion was evaluated at the last follow-up time. The patients were followed up for 12-24 months (averaged 19 months). The ODI, VAS and IH were significantly improved at 1 week postoperation and the last follow-up time compared with those at preoperative period (P<0.05). But there was no significant difference between 1 week postoperative and the last follow-up time (P<0.05). Brantigan's standard was used to evaluate fusion at the last follow-up time. There were 19 patients with grade 5 fusion, 8 with grade 4 fusion, with a fusion rate of 100%, and none with grade 1-3 fusions. There was no cage translocation and internal fixation breakage. These results suggested that n-HA/PA66 cage was an ideal biological material in the posterior lumbar interbody fusion and internal fixation operation for treatment of lumbar degenerative diseases. It can effectively maintain the intervertebral height and keep a high rate of bony fusion. The early clinical effect has been satisfactory.
ObjectiveTo summarize the research and application progress of magnesium and magnesium alloys implants in the orthopedics. MethodsThe domestic and foreign related literature about the research progress and application of magnesium and magnesium alloys implants in the orthopedics was reviewed. ResultsCurrently approved and commonly used metallic implants in orthopedics include stainless steels, titanium alloys, and chromium alloys having many disadvantages of poor biocompatibility, mismatch with the biomechanical properties of the bone tissue, and need of second surgical procedure to remove. Compared with traditional implants, magnesium and magnesium alloys have biomechanical properties closer to natural bone tissue, and in vivo degradation, which have the potential to serve as new biocompatible and degradable implants. Although magnesium and magnesium alloy materials have their own advantages, but the degradation rate is still too fast and so on. At present, the research and development of medical magnesium and magnesium alloy materials are to improve their corrosion resistance and control the rate of degradation. ConclusionMagnesium and magnesium alloys have great potential as a implant material in the orthopedics, through further systematic and in-depth study, it is expected to become a new generation of degradation biological implant materials.
ObjectiveTo observe the long-term outcome and biocompatibility of the porcine collagen membrane (DermalGen) after xenotransplantation in vivo.MethodsTwenty Sprague Dawley rats were randomly divided into 2 groups (n=10). DermalGen were implanted subcutaneously into the dorsum of rats in experimental group, and the rats in control group were treated with sham-operation. At 3, 7, and 15 days and 1, 3, 6, and 12 months after operation, the samples of experimental group were harvested and gross observation, histological observation, CD31 immunohistochemical staining, and transmission electron microscope observation were taken to observe the inflammatory reaction, angiogenesis, and collagen arrangement. The skin tissues of the control group at 12 months were observed and compared.ResultsAll incisions healed in experimental group, without obvious swelling and inflammatory reaction. The DermalGen was closely contact with the surrounding tissue without obvious rejection, and it was still legible at 12 months. Histological observation of experimental group showed that the infiltration of fibroblasts and inflammatory cells were seen at 7 days. More capillaries and fibroblast cells were seen and the inflammatory response gradually faded at 15 days and 1 month. There were abundant vessels and cells in the DermalGen at 3 months. The angiogenesis and fibroblasts decreased gradually, and the collagen started to format and margin blended simultaneously at 6 and 12 months. The inflammatory cells in experimental group at 15 days and 1 month were significantly more than that in control group (P<0.05), and no significant difference was found at 12 months between experimental group and control group (P>0.05). Immunohistochemical staining of experimental group showed that the angiogenesis changed obviously with the time, and the density of vessels decreased significantly at 12 months. Compared with control group, the possitive expressions of CD31 in experimental group at 15 days and 12 months after operation were significantly decreased (P<0.05), and were significantly increased at 1 month (P<0.05). Transmision electron microscope observation showed that the arrangement of collagen in grafted DermalGen had no obvious changed when compared with the DermalGen, and vascular endothelial cell, capillarypericytes and fibroblast cells could be seen inside.ConclusionThe DermalGen structure is stable after long-term xenotransplantation and with good tolerogenic property in vivo.
ObjectiveTo investigate the mechanical properties of the novel compound calcium phosphate cement (CPC) biological material as well as the biological activity and osteogenesis effects of induced pluripotent stem cells (iPS) seeding on scaffold and compare their bone regeneration efficacy in cranial defects in rats.MethodsAc- cording to the different scaffold materials, the experiment was divided into 4 groups: pure CPC scaffold group (group A), CPC∶10%wt chitosan as 2∶1 ratio mixed scaffold group (group B), CPC∶10%wt chitosan∶whisker as 2∶1∶1 ratio mixed scaffold group (group C), and CPC∶10%wt chitosan∶whisker as 2∶1∶2 ratio mixed scaffold group (group D). Mechanical properties (bending strength, work-of-fracture, hardness, and modulus of elasticity) of each scaffold were detected. The scaffolds were cultured with fifth generation iPS-mesenchymal stem cells (MSCs), and the absorbance (A) values of each group were detected at 1, 3, 7, and 14 days by cell counting kit 8 (CCK-8) method; the alkaline phosphatase (ALP) activity, Live/Dead fluorescence staining and quantitative detection, ALP, Runx2, collagen typeⅠ, osteocalcin (OC), and bone morphogenetic protein 2 (BMP-2) gene expressions by RT-PCR were detected at 1, 7, and 14 days; and the alizarin red staining were detected at 1, 7, 14, and 21 days. Twenty-four 3-month-old male Sprague Dawley rats were used to establish the 8 mm-long skull bone defect model, and were randomly divided into 4 groups (n=6); 4 kinds of scaffold materials were implanted respectively. After 8 weeks, HE staining was used to observe the repair of bone defects and to detect the percentage of new bone volume and the density of neovascularization.ResultsThe bending strength, work-of-fracture, hardness, and modulus of elasticity in groups B, C, and D were significantly higher than those in group A, and in groups C, D than in group B, and in group D than in group C (P<0.05). CCK-8 assay showed that cell activity gradually increased with the increase of culture time, theA values in groups B, C, and D at 3, 7, 14 days were signifiantly higher than those in group A, and in groups C, D than in group B (P<0.05), but no significant difference was found between groups C and D (P>0.05). Live/Dead fluorescence staining showed that the proportion of living cells in groups B, C, and D at 7 and 14 days was significantly higher than that in group A (P<0.05), and in groups C, D at 7 days than in group B (P<0.05); but no significant difference was found between groups C and D (P>0.05). RT-PCR showed that the relative expressions of genes in groups B, C, and D at 7 and 14 days were significantly higher than those in group A, and in groups C, D than in group B (P<0.05); but no significant difference was found between groups C and D (P>0.05). Alizarin red staining showed that the red calcium deposition on the surface of scaffolds gradually deepened and thickened with the prolongation of culture time; theA values in groups B, C, and D at 14 and 21 days were significantly higher than those in group A (P<0.05), and in groups C and D than in group B (P<0.05), but no significant difference was found between groups C and D (P>0.05).In vivo repair experiments in animals showed that the new bone in each group was mainly filled with the space of scaffold material. Osteoblasts and neovascularization were surrounded by new bone tissue in the matrix, and osteoblasts were arranged on the new bone boundary. The new bone in groups B, C, and D increased significantly when compared with group A, and the new bone in groups C and D was significantly higher than that in group B. The percentage of new bone volume and the density of neovascularization in groups B, C, and D were significantly higher than those in group A, and in groups C and D than in group B (P<0.05); but no significant difference was found between groups C and D (P>0.05).ConclusionThe mechanical properties of the new reinforced composite scaffold made from composite chitosan, whisker, and CPC are obviously better than that of pure CPC scaffold material, which can meet the mechanical properties of cortical bone and cancellous bone. iPS-MSCs is attaching and proliferating on the new reinforced composite scaffold material, and the repair effect of bone tissue is good. It can meet the biological and osteogenic activity requirements of the implant materials in the bone defect repair.