Objective To review the research progress of cell-scaffold complex in the tendon tissue engineering. Methods Recent literature concerning cell-scaffold complex in the tendon tissue engineering was reviewed, the research situation of the cell-scaffold complex was elaborated in the aspects of seed cells, scaffolds, cell culture, and application. Results In tendon tissue engineering, a cell-scaffold complex is built by appropriate seed cells and engineered scaffolds. Experiments showed that modified seed cells had better therapeutic effects. Further, scaffold functionality could be improved through surface modification, growth factor cure, mechanical stimulation, and contact guidance. Among these methods, mechanical stimulation revealed the most significant results in promoting cell proliferation and function. Through a variety of defect models, it is demonstrated that the use of cell-scaffold complex could achieve satisfactory results for tendon regeneration. Conclusion The cell-scaffold complex for tendon tissue engineering is a popular research topic. Although it has not yet met the requirement of clinical use, it has broad application prospects.
Objective To review the appl ication of electrospinning in preparation of tendon tissue engineered scaffolds, to describe its appl ication effect and prospects. Methods Recent l iterature was extensively reviewed and summarized from various aspects, concerning the appl ication of electrospinning in preparing tendon tissue engineered scaffolds. Results Because of its huge surface and high porosity, the electrospun fibers prepared by electrospinning technology have been widely used in the manufacture of tendon tissue engineered scaffolds in recent years. A variety of materials, including polylactic acid, have been successfully electrospun into various types of tendon tissue engineered scaffolds, and goodresults in the repair of tendon defect were achieved. Conclusion The electrospinning technology has provide a new way for the preparation of the tendon tissue engineered scaffolds, with the perfection of the technology they will have broad application prospects in the field of tendon tissue engineering.
Objective To investigate the cellular compatibil ity of polyvinyl alcohol (PVA)/wild antheraea pernyisilk fibroin (WSF), and to explore the feasibil ity for tendon tissue engineering scaffold in vitro. Methods The solutions of WSF (11%), PVA (11%), and PVA/WSF (11%) were prepared with 98% formic acid (mass fraction) at a mass ratio of 9 : 1. The electrospinning membranes of WSF, PVA, and PVA/WSF were prepared by electrostatic spinning apparatus. The morphologies of scaffolds were evaluated using scanning electronic microscope (SEM). The tendon cells were isolated from tail tendon of 3-dayold Sprague Dawley rats in vitro. The experiment was performed using the 3rd generation cells. The tendon cells (1 × 106/mL) were cocultured with PVA and PVA/WSF electrospinning film, respectively, and MTT test was used to assess the cell adhesion rate 4, 12 hours after coculture. The tendon cells were cultured in PVA and PVA/WSF extraction medium of different concentration (1, 1/2, and 1/4), respectively; and the absorbance (A) values were detected at 1, 3, 5, and 7 days to evaluate the cytotoxicity. The composite of tendon cells and the PVA or PVA/WSF scaffold were observed by HE staining at 7 days and characterized by SEM at 1,3, 5, and 7 days. Results The solution of WSF could not be used to electrospin; and the solution of PVA and PVA/WSF could be electrospun. After coculture of tendon and PVA or PVA/WSF electrospinning membranes, the cell adhesion rates were 26.9% ±0.4% and 87.0% ± 1.0%, respectively for 4 hours, showing significant difference (t=100.400, P=0.000); the cell adhesion rates were 35.2% ± 0.6% and 110.0% ± 1.7%, respectively for 12 hours, showing significant difference (t=42.500, P=0.000). The cytotoxicity of PVA/WSF was less significantly than that of PVA (P lt; 0.05) and significant difference was observed between 1/2 PVA and 1/4PVA (P lt; 0.05). HE staining and SEM images showed that the tendon cells could adhere to PVA and PVA/WSF scaffolds, but that the cells grew better in PVA/WSF scaffold than in PVA scaffold in vitro. Conclusion PVA/WSF electrospinning membrane scaffold has good cell compatibility, and it is expected to be an ideal scaffold of tendon tissue engineering.